I-3004 Ingxubevange yi-alloy ye-AL-Mn, eyona aluminium isetyenziswa kakhulu ekukhuseleni umhlwa.Amandla e-3004 aphezulu kune-3003. Amandla ale alloy ayiphezulu kwaye ayikwazi ukuphathwa ngobushushu.Ngoko ke, indlela yonyango ebandayo isetyenziselwa ukuphucula iimpawu zomatshini.I-3003 ine-plastiki ephezulu kwimo edibeneyo, ukuxhathisa okulungileyo kokubola kunye ne-weldability efanelekileyo.I-Aluminiyam ye-3004 isetyenziswa ngokubanzi kwiindawo zokulungisa ezifuna ukubunjwa okulungileyo, ukuxhathisa okuphezulu kwe-corrosion kunye ne-solderability.
Ukwakheka kwemichiza WT(%) | |||||||||
Isilicon | Intsimbi | Ubhedu | Magnesium | IManganese | Chromium | Zinc | I-Titanium | Abanye | Aluminiyam |
0.3 | 0.7 | 0.25 | 0.8~1.3 | 1~1.5 | - | 0.25 | - | 0.15 | Ibhalansi |
Iipropati zoomatshini eziqhelekileyo | |||
Ukutyeba (mm) | Tensile strength (Mpa) | Unikeze Amandla (Mpa) | Elongation (%) |
0.5~250 | 150~285 | 60-240 | 1-16 |
Usetyenziso
ITanki yokuGcina
Isinki yobushushu
Izinto zokwakha
Inzuzo Yethu
Uluhlu kunye nokuhanjiswa
Sinemveliso eyaneleyo kwisitokhwe, sinokunikela ngezinto ezaneleyo kubathengi.Ixesha lokukhokela linokuba phakathi kweentsuku ezi-7 kwizinto eziphathekayo.
Umgangatho
Zonke imveliso zivela kumvelisi omkhulu, sinokunikezela ngeMTC kuwe.Kwaye sinokunikezela ngengxelo yovavanyo lweQela leSithathu.
Isiko
Sinomatshini wokusika, ubukhulu besiko buyafumaneka.