China wholesale Aluminum Bar - 4032 Aluminum Plate – Miandi
China wholesale Aluminum Bar - 4032 Aluminum Plate – Miandi Detail:
4032 Aluminum Alloy has large thermal expansion coefficient, with high strength and corrosion resistance in high temperature environments. 4032 aluminum alloy is used to machine forged pistons.
|
Chemical Composition WT(%) |
|||||||||
|
Silicon |
Iron |
Copper |
Magnesium |
Manganese |
Chromium |
Zinc |
Titanium |
Others |
Aluminum |
|
11.0~13.5 |
1.0 |
0.05~1.3 |
0.8~1.3 |
0.5~1.3 |
0.1 |
0.25 |
- |
0.15 |
Balance |
|
Typical Mechanical Properties |
|||
|
Thickness (mm) |
Tensile Strength (Mpa) |
Yield Strength (Mpa) |
Elongation (%) |
|
0.5~250 |
≥315 |
≥380 |
≥9 |
Applications
Piston
Our Advantage
Inventory and Delivery
We have enough product in stock, we can offer enough material to customers. The lead time can be within 7 days for stock materil.
Quality
All the product are from the biggest manufacturer, we can offer the MTC to you. And we can also offer Third-Party test report.
Custom
We have cutting machine, custom size are available.
Product detail pictures:
Related Product Guide:
Gigging the night away, thanks to tighter regulations | A7075 Aluminum Sheet
Life Proof delivers patrol boat to North Carolina | Aluminum 5086
Our commission would be to serve our customers and clientele with very best excellent and aggressive portable digital products for China wholesale Aluminum Bar - 4032 Aluminum Plate – Miandi , The product will supply to all over the world, such as: Canada, Bandung, Armenia, To get more information about us as well as see all our products, please visit our website. To get more information please feel free to let us know. Thank you very much and wish your business always be great!
By Michelle from Lahore - 2018.12.22 12:52
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Hilary from Philippines - 2018.12.10 19:03