Ngefomu lepuleti, i-6082 iyingxubevange evame ukusetshenziselwa ukukhanda okuvamile.Isetshenziswa kabanzi e-Europe futhi ithathe indawo ye-6061 alloy ezinhlelweni eziningi, ikakhulukazi ngenxa yamandla ayo aphezulu (kusuka enanini elikhulu le-manganese) kanye nokumelana kwayo okuhle kakhulu nokugqwala.Ngokuvamile kubonakala kwezokuthutha, izikafula, amabhuloho kanye nobunjiniyela obujwayelekile.
| I-Chemical Composition WT(%) | |||||||||
| I-silicon | Insimbi | Ithusi | Magnesium | IManganese | I-Chromium | Zinc | I-Titanium | Abanye | I-Aluminium |
| 0.7~1.3 | 0.5 | 0.1 | 0.6~1.2 | 0.4~1.0 | 0.25 | 0.2 | 0.1 | 0.15 | Ibhalansi |
Izinhlobo Zokufutheka
Intukuthelo evame kakhulu ye-6082 alloy yilezi:
F - Njengoba yenziwe.
I-T5 - Ipholiswe kusukela kunqubo yokuma kwezinga lokushisa ephakeme futhi iguge ngokuzenzisa.Kusebenza emikhiqizweni engabandi esetshenziwe ngemuva kokupholisa.
I-T5511 - Ipholiswe enqubweni yokwakheka kwezinga lokushisa eliphakeme, ingcindezi edanjiswa ukwelula nokuguga ngokuzenzela.
I-T6 - Isixazululo siphathwa ngokushisa futhi siguge ngokuzenzela.
U-O-Anealed.Lawa amandla aphansi kakhulu, ulaka oluphakeme kakhulu lwe-ductility.
I-T4 - Kulashwe ukushisa kwesixazululo futhi kuguge ngokwemvelo kuze kube sesimweni esizinzile kakhulu.Isebenza emikhiqizweni engabandi esetshenzwe ngemuva kokwelashwa kokushisa kwesixazululo.
I-T6511 - Kulashwe ukushisa kwesixazululo, ingcindezi idambiswe ukwelula, nokuguga ngokuzenzela.
| Izakhiwo Zemishini Ejwayelekile | ||||
| Ulaka | Ubukhulu (mm) | Amandla Okuqina (Mpa) | Isivuno Amandla (Mpa) | Ukwelula (%) |
| T4 | 0.4~1.50 | ≥205 | ≥110 | ≥12 |
| T4 | 1.50 ~ 3.00 | ≥14 | ||
| T4 | 3.00 ~ 6.00 | ≥15 | ||
| T4 | 6.00 ~ 12.50 | ≥14 | ||
| T4 | 12.50 ~ 40.00 | ≥13 | ||
| T4 | ＞40.00–80.00 | ≥12 | ||
| T6 | 0.4~1.50 | ≥310 | ≥260 | ≥6 |
| T6 | 1.50 ~ 3.00 | ≥7 | ||
| T6 | 3.00 ~ 6.00 | ≥10 | ||
| T6 | 6.00 ~ 12.50 | ≥300 | ≥255 | ≥9 |
Ingxubevange 6082 Properties
I-alloy 6082 inikeza izici ezifanayo, kodwa ezingalingani, ezingokomzimba ku-6061 ingxubevange, kanye nezakhiwo eziphakeme kancane zemishini esimweni -T6.Inezici ezinhle zokuqeda futhi iphendula kahle emigqumeni evame kakhulu ye-anodic (okungukuthi, ecacile, ecacile futhi edayi, i-hardcoat).
Izindlela ezehlukene zokuhlanganisa ezentengiselwano (isb., ukushisela, ukubhinca, njll.) zingasetshenziswa ku-alloy 6082;Nokho, ukwelashwa ukushisa kungase kunciphise amandla endaweni weld.Ihlinzeka ngokusebenza kahle kwe--T5 kanye ne-T6 tempers, kodwa ama-chip breaker noma amasu okumaka akhethekile (isb., ukubhoboza i-peck) ayanconywa ukuze kuthuthukiswe ukwakheka kwe-chip.
I--0 noma -T4 temper iyatuswa uma ugoba noma wenza ingxubevange engu-6082. Kungase futhi kube nzima ukukhiqiza izimo ezincane ze-extrusion ezinezindonga ku-6082 alloy, ngakho-ke i-T6 temper ingase ingatholakali ngenxa yemikhawulo yokucisha ingxubevange.
Isebenzisa i-6082 Alloy
Ukushisela okuhle kwe-alloy 6082, i-brazeability, ukumelana nokugqwala, ukwakheka kanye nokusebenza kahle kwemishini kuyenza isebenziseke ezintongeni, ibha kanye nesitokwe somshini, amashubhu e-aluminium angenamthungo, amaphrofayili esakhiwo kanye namaphrofayili angokwezifiso.
Lezi zici, kanye nesisindo sazo esilula kanye nezakhiwo ezinhle kakhulu zemishini, zibe nomthelela ekusetshenzisweni kwe-alloy 6082-T6 ezimotweni, zezindiza kanye nezicelo zesitimela esinesivinini esikhulu.